<Description>
M-15 29 Ga
Non-oriented silicon steel


<B-H curve> at 20*C
% H(A/m)       B(T)
0              0
72.33592164    0.7526
74.39697815    0.7716
76.57740087    0.7907
78.85331655    0.8098
81.16902098    0.8289
83.55634512    0.8479
86.10282421    0.867
88.72888077    0.8861
91.51409228    0.9052
94.5380362     0.9242
97.64155759    0.9433
100.9042339    0.9624
104.1669103    0.9815
107.5887415    1.001
111.2493052    1.02
115.3077563    1.039
119.8436721    1.058
124.6978979    1.077
129.950011     1.096
135.679589     1.115
141.9662092    1.134
149.1281817    1.153
157.4838162    1.172
166.8739578    1.191
177.1394517    1.21
188.5190301    1.229
201.8084678    1.249
217.4056523    1.268
234.5148086    1.287
254.5683315    1.306
281.6246718    1.325
314.0922802    1.344
347.9922831    1.363
392.4760897    1.382
446.190883     1.401
520.1979315    1.42
615.8500523    1.439
746.595838     1.458
881.7183847    1.477
1054.401498    1.496
1241.408556    1.515
1480.936745    1.534
1748.31705     1.553
2064.239612    1.572
2427.908657    1.59
2814.655169    1.609
3263.472108    1.628
3791.070744    1.647
4399.042627    1.665
5024.521553    1.684
5692.17654     1.703
6386.092092    1.722
7136.507648    1.74
7957.747155    1.759
8825.141594    1.778
9803.944494    1.796
10894.15585    1.815
12032.1137     1.834
13241.69127    1.852
14650.21251    1.871
16233.8042     1.89
18024.29731    1.908
20172.88904    1.926
22536.33994    1.944
25210.14299    1.961
28440.98833    1.979
31974.22807    1.996
36279.36928    2.012
41595.14438    2.027
47404.2998     2.041
53762.53978    2.056
61266.69534    2.069


<Iron loss>
%Steinmetz coefficients
0.0227288148583325       % kh
1                        % alfa
1.77364043109264         % beta
2.11492029537421e-05     % Ke


<Mass Density> (kg/m^3)
7650